Features
Excellent Physical Properties
Provides flexible and durable repairs. It is impact-resistant and protects the base material. Additionally, it helps reduce noise. It can withstand temperatures up to 80°C, making it suitable for various environments.
Versatile Repair and Protection
Extends the lifespan of rubber components by overlay repairs. Highly resistant to impact and wear, it is effective for sealing leaks in vibrating equipment. It can also bond rubber materials together for flexible repairs.
Easy and Efficient Application
Simple to apply and mix; its paste-like consistency makes it suitable for wall surfaces. It cures quickly, allowing for fast and efficient repairs. It can be evenly applied to various component shapes and sizes.
Chemical Resistance
| Chemical | Usability |
|---|---|
| Ethanol | ○ |
| Acetone | × |
| Nitrite | ○ |
| Gasoline | ○ |
| Benzine | ○ |
| Toluene | ○ |
| Xylene | ○ |
| Hydrochloric Acid | ○ |
| Sulfuric Acid | ○ |
| Phosphoric Acid | ○ |
| Sodium Hydroxide | ○ |
Specifications
| Item | Main Agent | Hardener |
|---|---|---|
| Mixing Ratio | 9:1 | |
| Color | Yellow Transparent | Black |
| Viscosity | 20,000–20,040 mPa·s | 00–240 mPa·s |
| Usable Time (300g, 25°C) | 6–9 minutes after mixing | |
| Tack-Free Time (5mm thickness, 25°C) | 30–40 minutes | |
| Curing Time (5mm thickness, 25°C) | 7–10 hours | |
| Specific Gravity | 1.02 | - |
| Hardness | Shore A80 (JIS K 7215) | - |
| Tensile Strength | 10–14 MPa (JIS K 7113) | - |
| Elongation | 400–450% (JIS K 7113) | - |
| Tear Strength | 52–59 N/mm (JIS K 7113) | - |
| Tensile Shear Adhesion Strength | Cohesive Failure: 6.2 MPa / Interface Peeling: 0.6 MPa | - |
| Heat Resistance | 80°C | - |
| Applicable Area | 0.118 m² | - |
| Set Contents | 0.54 kg | 0.06 kg |
Applications
- Repair of rubber parts such as conveyor belts and bellows
- Restoration of airtight performance in butterfly valves and manholes
- Leak repairs on vibrating pipes, flanges, and boxes
- Noise prevention from metal collisions in parts feeders
- Protection of impact-exposed surfaces such as pumps, chutes, and centrifuges
- Bonding of rubber materials